M.O. Durowoju  , 
    Fractal Analysis of the Pores in Annealed Al-V<SUB>2</SUB>O<SUB>5</SUB> Mechanically Alloyed Composite,
    Journal of Engineering and Applied Sciences,
    Volume 2,Issue 10,
    2007,
    Pages 1489-1492,
    ISSN 1816-949x,
    jeasci.2007.1489.1492,
    (https://makhillpublications.co/view-article.php?doi=jeasci.2007.1489.1492)
    Abstract: Fractal analysis was used to observe the size, shape and distribution of pores in Al-V<SUB>2</SUB>O<SUB>5 </SUB>mechanically alloyed composite. The analysis reveals that the pores are of irregular shapes, i.e shrinkage pores, with sphericity   &lt; 0.3.The `worst` of the shapes is the pore with   = 1.0254e-009 and D = 1.8541, while the `best` shape is the pore with   = 4.8309e-004 and D = 1.6521. Also, the graph of   against D shows that as   decreases the D values increases. This is in agreement with the theoretical background.
    Keywords: Fractal analysis;microstructures;composites;fractal dimension;pores