Abstract
In this study, cobalt and copper ferrite compounds were prepared by co-precipitation method, the nanocompound (CoxCu1–xFe2O4) was then prepared by mixing cobalt ferrite and copper ferrite with different ratios of cobalt. The structural, morphological and magnetic properties of the resulted nanoparticles were studied. The XRD measurements showed dominant and high peaks located at 35.54° and 35.31° belong to the (311) CoFe2O4 and (211) CuFe2O4 planes, respectively at the same time, a decrease in grain size was observed with an increase in the ratio of copper ferrite as well as a decrease in the expansion of the magnetic hysteresis ring by increasing copper ratio.
How to cite this article:
Saleh H. Abud, Ali Kitab Attia and Raheem Abed Jeber. The Deflection of the Magnetic Ring for the Magnetic System CoxCu1–xFe2O4.